Photocatalytic behavior for the phenol degradation of ZnAl layered double hydroxide functionalized with SDS.

Functionalized ZnAl layered double hydroxide based photocatalyst was obtained by the addition of sodium dodecyl sulfate (SDS) during the synthesis by the coprecipitation method, and further calcination at 400 °C. Bare and modified materials were characterized by X-ray diffraction, nitrogen adsorption-desorption, IR, UV-Vis, EPR and XPS spectroscopies, SEM and HRTEM. The synthesized material was evaluated in the photodegradation of phenol in a 40 ppm aqueous solution (4.25 × 10-4 mol of phenol/L), under UV light irradiation. An increasing in the degradation of phenol from 62 to 95%, and from 62 to 82% in the mineralization of phenol was obtained using SDS functionalized ZnAl LDH, in comparison with the unmodified material. This increase could be attributed to the presence of sulfate radicals, confirmed by the EPR study.

Transformation of Nanostructures Cu2O to Cu3Se2 through Different Routes and the Effect on Photocatalytic Properties.

In this work, copper selenide (Cu3Se2 umangite phase) was synthesized by two routes, using a chemical reaction and the hydrothermal method to obtain CuSe-A and CuSe-H, respectively. The synthesis of Cu3Se2 consisted of a three-step process: in the first step, copper(I) oxide hexapods (Cu2O) were obtained as the copper reservoir; in the second step, selenium ions were obtained from the reduction of selenium powder; and in the third step involves mixing two precursors following the two synthesis routes mentioned before. Analysis of X-ray diffraction and X-ray photoelectron spectroscopy showed the formation of the Cu3Se2 phase by both synthesis routes. On the other hand, using the scanning electron microscopy (SEM) technique, it is observed that the Cu3Se2 sample (CuSe-A) is obtained by exchanging in solution with agitation and that the copper selenium phase grows only on the surface of the hexapods. Meanwhile, the hydrothermal route promotes a total conversion of copper(I) oxide hexapods to the copper selenide phase (CuSe-H). The resulting materials were tested as photocatalytic materials to remove methylene blue dye in water under sunlight irradiation. Cu3Se2 (CuSe-H) obtained by the hydrothermal route exhibited a higher efficiency of photodegradation of dye, reaching a removal percentage of 92% after 4 h under sunlight.